Emitter saturation current densities of 22 fA/cm 2 applied to industrial PERC solar cells approaching 22% conversion efficiency
Author(s) -
Dullweber Thorsten,
Hannebauer Helge,
Dorn Silke,
Schimanke Sabrina,
Merkle Agnes,
Hampe Carsten,
Brendel Rolf
Publication year - 2017
Publication title -
progress in photovoltaics: research and applications
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 2.286
H-Index - 131
eISSN - 1099-159X
pISSN - 1062-7995
DOI - 10.1002/pip.2806
Subject(s) - common emitter , saturation current , materials science , analytical chemistry (journal) , doping , current density , saturation (graph theory) , energy conversion efficiency , optoelectronics , voltage , chemistry , electrical engineering , physics , mathematics , chromatography , quantum mechanics , combinatorics , engineering
Passivated Emitter and Rear Cells (PERC) are currently being introduced into mass production. The conversion efficiency of industrial p ‐type PERC cells is limited by the emitter saturation current density of around 90 fA/cm 2 of conventional homogeneously POCl 3 diffused emitters. In this paper we investigate two alternative emitter formation technologies. The first approach named in‐situ oxidation inserts a short thermal oxidation in‐between the phosphorus silicate glass deposition and the drive‐in of a conventional homogeneous POCl 3 diffusion thereby reducing the phosphorus surface concentration. The second approach named Gas Phase Etch Back (GEB) selectively removes around 40 nm of the highly doped surface of the POCl 3 diffused emitter by the reactive gas phase of the wet chemical rear polishing bath. Whereas the conventional POCl 3 emitter exhibits a phosphorus surface doping concentration of 3 × 10 20 cm −3 , the in‐situ oxidation and the GEB process reduce the doping concentration to 7 × 10 19 cm −3 and 4 × 10 19 cm −3 , respectively. Accordingly, the emitter saturation current density is reduced to excellent values of 22 fA/cm 2 ( in‐situ oxidation) and 28 fA/cm 2 (GEB) compared with 89 fA/cm 2 for the reference POCl 3 diffusion. Whereas the reference POCl 3 emitter limits the PERC conversion efficiency η to 21.1% and the open circuit voltage V oc to 655 mV, the in‐situ oxidation improves the PERC current–voltage parameters up to 21.3% and 663 mV. The highest efficiency of 21.6% is obtained with the selective GEB emitter. When solving series resistance issues with the most advanced GEB emitter, the measured V oc and J sc values would support PERC conversion efficiencies up to 21.9%. Copyright © 2016 John Wiley & Sons, Ltd.