Effect of isomerization on thermal behaviour of bisitaconimides

The effect of isomerization of N , N ′‐bisitaconimido‐4,4′‐diphenyl ether to the corresponding biscitraconimide on the curing characteristics and thermal stability of cured resins is described. Resins having bisitaconimide:biscitraconimide ratios of 23:77–93:7 were prepared by reacting 4,4′‐diaminodiphenyl ether with itaconic anhydride in solvents of different polarities and under different reaction conditions. Resins containing a higher proportion of citraconimide had a lower melting point (191 vs 208 °C). The curing exotherm was observed immediately after melting in all the resins and exothermic peak temperature reduced with increase in citraconimide content. Resins having a higher proportion of citraconimide on isothermal curing (200 °C, 2 h) and subsequent heating in nitrogen atmosphere degraded at a slightly lower temperature. However, the char yield at 800 °C did not show any systematic dependence on citraconimide content. © 2002 Society of Chemical Industry