Effect of filler loading on cure time and swelling behaviour of SMR L/ENR 25 and SMR L/SBR blends
Author(s) -
Ismail Hanafi,
Poh B T,
Tan K S,
Moorthy M
Publication year - 2003
Publication title -
polymer international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.592
H-Index - 105
eISSN - 1097-0126
pISSN - 0959-8103
DOI - 10.1002/pi.1002
Subject(s) - carbon black , materials science , swelling , calcium carbonate , filler (materials) , composite material , carbon fibers , composite number , natural rubber
The effect of filler loading on the cure time ( t 90 ) and swelling behaviour of SMR L/ENR 25 and SMR L/SBR blends has been studied. Carbon black (N330), silica (Vulcasil C) and calcium carbonate were used as fillers and the loading range was from 0 to 40 phr. Results show that for SMR L/ENR 25 blends the cure time decreases with increasing carbon black loading, whereas silica shows an increasing trend, and calcium carbonate does not show significant changes. For SMR L/SBR blends, the cure time of carbon black, silica and calcium carbonate generally decreases with increasing filler loading. The percentage swelling in toluene and ASTM oil no 3 decreases for both blends with increasing filler loading, with calcium carbonate giving the highest value, followed by silica‐ and carbon black‐filled blends. At a fixed filler loading, SMR L/ENR 25 blend shows a lower percentage swelling than SMR L/SBR blends. © 2003 Society of Chemical Industry