Linear low density polyethylenes and their blends: Part 4 shear flow of LLDPE blends with LLDPE and LDPE
Author(s) -
Utracki L. A.,
Schlund B.
Publication year - 1987
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.760272006
Subject(s) - linear low density polyethylene , materials science , low density polyethylene , miscibility , die swell , composite material , rheology , rheometry , polyethylene , shear modulus , dynamic mechanical analysis , polymer blend , viscoelasticity , polymer , extrusion , copolymer
The steady state and dynamic shear behavior of linear low density polyethylenes (LLDPE) blended with low density polyethylene (LDPE) and with another LLDPE resin were measured in capillary and parallel plate geometries at T = 150, 190, and 230°C. The extrudate swell and the Bagley correction were determined. It was observed that the pressure correction plays a significant role in capillary flow of LLDPE/LDPE blends–an indication of immiscibility. Several other rheological functions also suggested a phase separation for the system. Nevertheless, the blend behaved as a “compatible” mixture of emulsion type. By contrast, blends of two LLDPE resins show expected miscibility. However, even in this case additivity was not always observed. A new simple method of calculating the relaxation spectrum was developed. The method is analytical and its accuracy depends on adequacy of the semiempirical relation (proposed previously) to describe dynamic viscosity dependence on the test frequency. For all samples the spectrum allowed computation of storage modulus in good agreement with experimental findings.