Effects of composition and polymerization mechanism on the mechanical properties of uv‐cured crosslinked polymers
Author(s) -
Levy N.,
Massey P. E.
Publication year - 1981
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.760210707
Subject(s) - photoinitiator , monomer , materials science , polymer , coating , polymerization , plasticizer , polymer chemistry , chemical engineering , photopolymer , reaction mechanism , composite material , organic chemistry , chemistry , catalysis , engineering
The effect of compositional variables on the mechanical properties of a UV‐cured coating was investigated. The coating contains two monomers, 2‐ethoxyethoxyethylacrylate (EEEA) and N‐vinyl‐pyrrolidone (NVP), and a higher molecular weight resin (MW ∼1000) which is a commercial urethane diacrylate. In addition, a photoinitiator, 2,2‐dimethoxy‐2‐phenylacetophenone, was present at a constant concentration. It was found that the mechanical properties of the cured films depend mainly on the concentration of 2‐ethoxyethoxyethylacrylate (EEEA). Spectroscopic analysis. showed that EEEA undergoes both homopolymerization as well as an addition reaction with the photoinitiator and is thus not incorporated in the crosslinked matrix but rather acts similar to a compatible plasticizer. Kinetic analysis of the reactions of the single components and mixtures showed widely diverging reactivities of the components with homopolymerization of EEEA being a favored reaction path. A speculative conclusion is that, to avoid homopolymerization and monomeric reactions, optimized coating formulations (coatings with mechanical properties that are not affected by small compositional variations) should be based on monomers and oligomers with similar reactivities.