Studies on structural foam processing I. The rheology of foam extrusion
Author(s) -
Han Chang Dae,
Villamizar C. A.
Publication year - 1978
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.760180904
Subject(s) - materials science , blowing agent , extrusion , bubble , polymer , composite material , polystyrene , viscosity , foaming agent , rheology , mechanics , physics , porosity , polyurethane
An experimental study was carried out to investigate the flow behavior of gas‐charged molten polymers in foam extrusion. For the study, a rectangular slit die with glass windows was constructed to permit visual observations, from the direction perpendicular to flow, of the dynamic behavior of gas bubbles when a gas‐charged molten polymer flows between two parallel planes. Pictures were taken of gas bubbles in the flow channel with the aid of a camera attached to a microscope, and these were later used to determine the position at which gas bubbles start to grow. Using three melt pressure transducers mounted on the short side of the rectangular slot, pressure distributions were measured along the longitudinal centerline of the die. The polymeric materials used were high‐density polyethylene and polystyrene, and the chemical blowing agents used were a proprietary hydrazide which generates nitrogen, and sodium bicarbonate which generates carbon dioxide. It was observed that the gas‐charged molten polymer shows a curved pressure profile as the melt approaches the die exit, whereas the polymer without a blowing agent shows a linear pressure profile. The visual observations of the bubble growth in the flow channel, together with the pressure measurements, permitted us to determine the bubble inflation pressure, often referred to as the critical pressure for bubble inflation. It was found that the critical pressure decreases with increasing melt extrusion temperature, and increases with increasing blowing agent concentration. It was also found that the bulk viscosity of gas‐charged molten polymers decreases with increasing blowing agent concentration and with increasing melt temperature. A general remark is made concerning the precaution one should take when an Instron rheometer is used for determining the bulk viscosity of gas‐charged molten polymers.