The influence of diblock copolymers on the structure and properties of polybutadiene‐polyisoprene blends
Author(s) -
Ramos A. R.,
Cohen R. E.
Publication year - 1977
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.760170823
Subject(s) - materials science , polybutadiene , copolymer , ternary operation , phase (matter) , polymer blend , polymer , casting , phase diagram , polymer chemistry , composite material , organic chemistry , chemistry , computer science , programming language
Abstract The structure and properties of a ternary polymer system comprised of 1, 4 polybutadiene, cis 1, 4 polyisoprene, and the corresponding 1, 4 polybutadiene/cis 1, 4 polyisoprene diblock copolymer have been investigated. Dynamic mechanical properties were measured as a function of frequency (3.5 to 110 Hz) and temperature (−135 to 40°C). Thermomechanical analysis and transmission electron microscopy provided additional information on the, phase relationships in the various specimens. The blends studied covered the entire triangular composition diagram; both slow solvent evaporation and rapid spin casting techniques were employed in the sample preparation. Results indicate that the BI diblock is a single phase material whereas binary blends of the two homopolymers are two‐phase in nature. Ternary blends of the two homopolymers with diblock and binary blends of a single homopolymer with diblock can be one or two phase materials depending on the sample composition and the ratio of B to I units in the diblock. All evidence From the dynamic, thermomechanical and microscopic experiments is used to elucidate the influence of the diblock in these polymer blends.