Residual stresses in polymers and their effect on mechanical behavior
Author(s) -
So Paul,
Broutman Lawrence J.
Publication year - 1976
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.760161202
Subject(s) - materials science , residual stress , composite material , polycarbonate , ultimate tensile strength , bending , polymer , quenching (fluorescence) , deformation (meteorology) , quantum mechanics , fluorescence , physics
Abstract Plates of bisphenol‐A polycarbonate and poly(methyl methacrylate) have been quenched in ice water from temperatures slightly above their glass transition temperatures. Residual stresses are thus created, Measurement of these residual stresses has been accomplished by the “layer removal” method and the stress distributions through the thickness are presented. Compressive stresses, approximately 3000 psi, exist at the surface while tensile stresses‐of at least 1000 psi exist in the interior. It is shown that these residual stresses can influence the notched Izod impact strengths for polycarbonates. The mechanism is thought to be suppression of craze initiation in advance of the notch due to the presence of residual compressive stresses for specimens notched prior to quenching. In the case of poly(methyl methacrylate), it is shown that compressive residual stresses at the surface can cause plastic yielding to occur in bending experiments resulting in permanent deformation and greater energy absorption.