Preparation of microcellular thermoplastic polyurethane (TPU) foam and its tensile property
Author(s) -
Ge Chengbiao,
Wang Shiping,
Zheng Wenge,
Zhai Wentao
Publication year - 2018
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.24813
Subject(s) - materials science , thermoplastic polyurethane , ultimate tensile strength , composite material , polyurethane , blowing agent , microstructure , scanning electron microscope , crystallinity , tensile testing , thermoplastic , elastomer
In this study, the thermoplastic polyurethane (TPU) composed of same type soft and hard segment while different hard segment contents was selected to prepare microcellular TPU foams, using CO 2 as the physical blowing agent in a batch foaming process. The TPU with high hard segment content (i.e., 36.1 wt%) exhibited high complex viscosity, low initial CO 2 content, and microcrystalline region, while the others (i.e., 32.0 and 26.1 wt%) showed opposite results. The cell structure evolution of TPU foams with the foaming temperature and the foaming time showed that the low hard segment content was benefiting for the expansion ratio, whereas the high hard segment content generated the microcrystalline region acting as the nucleating site to improve the cell density. The tensile behavior of prepared TPU foams was investigated in the cyclic tensile test. It was observed that the hysteresis and residual strain increased with the increasing hard segment content, furtherly exhibited lower value compared to TPU. Moreover, scanning electron microscopy, differential scanning calorimeter, and infrared spectra were used to reveal the microstructure after tensile test. The results indicated that the cell structures had a significant contribution to improve the elasticity, resulting from the protection of cells on the hard domains. POLYM. ENG. SCI., 58:E158–E166, 2018. © 2017 Society of Plastics Engineers