Molecularly imprinted poly(acrylonitrile‐ co ‐acrylic acid) matrix with sclareol
Author(s) -
Dima StefanOvidiu,
Dobre Tanase,
Chetraru Olga,
Nicolae CristianAndi,
Spataru CatalinIlie,
Sarbu Andrei
Publication year - 2014
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.23689
Subject(s) - acrylonitrile , copolymer , materials science , differential scanning calorimetry , acrylic acid , molecularly imprinted polymer , molecular imprinting , thermogravimetric analysis , monomer , polymer chemistry , polymer , chemical engineering , nuclear chemistry , organic chemistry , chemistry , selectivity , composite material , catalysis , physics , engineering , thermodynamics
There are presented results regarding a new set of molecularly imprinted polymers (MIPs) based on acrylonitrile:acrylic acid (AN:AA) copolymer matrix. As template, it was used sclareol, an important anticancer bioactive compound, never used before for molecular imprinting. An emerging and insufficient studied MIP preparation method, namely the phase inversion, was used to prepare 0.8 mm spherical sclareol MIPs (S‐MIPs). Three AN:AA copolymers, having the initial monomer ratios 90:10, 80:20, and 70:30, were synthesized by radical copolymerization in emulsion, without emulsifier. After that, each copolymer was dissolved in the presence of the template (sclareol) in dimethylformamide. The imprinting and the morphology of these new materials were analyzed by rheology, elemental analysis, infrared spectroscopy, size exclusion chromatography, thermogravimetric analysis, differential scanning calorimetry, batch rebinding tests, and Scatchard analysis. The conclusion was that the AN:AA‐80:20 matrix proved to be the optimized solution between high rigidity (given by the AN segments) and high affinity for the template (given by AA segments), the average imprinting factor for this system being 2.67. POLYM. ENG. SCI., 54:1484–1494, 2014. © 2013 Society of Plastics Engineers