Static and dynamic compressive properties of polypropylene/zinc oxide nanocomposites
Author(s) -
Omar Mohd Firdaus,
Akil Hazizan Md,
Ahmad Zainal Arifin,
Mahmud Shahrom
Publication year - 2014
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.23633
Subject(s) - polypropylene , materials science , composite material , nanocomposite , strain rate , zinc , split hopkinson pressure bar , oxide , particle (ecology) , polymer nanocomposite , metallurgy , oceanography , geology
The effect of strain rate is widely recognized as an essential factor that influences the mechanical properties of polymer matrix composites. Despite its importance, no previous work has been reported on the high‐strain rate behavior of polypropylene/zinc oxide nanocomposites. Based on this, static and dynamic compression properties of polypropylene/zinc oxide nanocomposites, with particle contents of 1%, 3%, and 5% by weight, were successfully studied at different strain rates (i.e., 0.01 s −1 , 0.1 s −1 , 650 s −1 , 900 s −1 , and 1100 s −1 ) using a universal testing machine and a split Hopkinson pressure bar apparatus. For standardization, approximately 24 nm of zinc oxide nanoparticles were embedded into polypropylene matrix for each of the tested polypropylene/zinc oxide nanocomposites. Results show that the yield strength, the ultimate strength, and the stiffness properties, of polypropylene/zinc oxide nanocomposites, were greatly affected by both particle loading and applied strain rate. Furthermore, the rate sensitivity and the absorbed energy of all tested specimens showed a positive increment with increasing strain rate, whereas the thermal activation volume showed a contrary trend. In addition, the fractographic analysis and particle dispersion of all composite specimens were successfully obtained using a field emisission scanning electron microscopy. POLYM. ENG. SCI., 54:949–960, 2014. © 2013 Society of Plastics Engineers