Conductive polypyrrole composite films prepared using wet cast technique with a pyrrole–cellulose acetate solution

Conductive polypyrrole‐cellulose acetate films were prepared from cellulose acetate (CA) solution of pyrrole (Py) using wet cast method. In the composite films, Py was used as a solvent for CA which was dissolved with different concentration. Then, to prepare PPy–CA composite film, the Py viscous solution of CA was cast on glass plate and immersed in FeCl 3 aqueous solution. When the CA film was formed in the aqueous solution, the polymerized PPy particles having about 1 μm diameter were formed in composite film. The resultant composite films were characterized, showing good film fabrication and electrical conductivity of around 6.9 × 10 −4 to 3.6 × 10 1 S/cm. POLYM. ENG. SCI., 54:78–84, 2014. © 2013 Society of Plastics Engineers