Totally bioresorbable composites prepared from poly( l ‐lactide)‐ co ‐(trimethylene carbonate) copolymers and poly( l ‐lactide)‐ co ‐(glycolide) fibers as cardiovascular stent material
Author(s) -
Han Yaru,
Jin Xiaoyun,
Yang Jian,
Fan Zhongyong,
Lu Zhiqian,
Zhang Yong,
Li Suming
Publication year - 2012
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.22137
Subject(s) - materials science , ultimate tensile strength , composite material , differential scanning calorimetry , lactide , copolymer , composite number , surface roughness , polymerization , polymer , physics , thermodynamics
This paper aims to evaluate the potential of totally bioresorbable composites as cardiovascular stent material. Copolymers were synthesized by ring‐opening polymerization of L ‐lactide (LLA) and 1,3‐trimethylene carbonate (TMC) with LLA‐TMC ratios of 3/1, 4/1, and 5/1 and characterized by nuclear magnetic resonance (NMR), gel permeation chromatography (GPC), and differential scanning calorimetry (DSC). Wt. 5% of poly( L ‐lactide)‐ co ‐(glycolide) (PLGA) fibers are used to reinforce PTMC‐LLA copolymer matrices to prepare totally bioresorbable composites. Heat treatment under vacuum and oxygen plasma treatment are applied to improve the mechanical performance of the composites in terms of eliminating the imperfections inside, enhancing interfacial affinity, surface roughness, and enriching surface oxidative chemical bonds. After plasma treatment, the viscosity and tensile strength of the fibers decrease, but the surface chemical bonds are enriched and surface roughness is increased. The composites with 15‐min plasma‐treated fibers and 2 h heat treatment exhibit the highest tensile strength of 46 MPa, i.e., very close to that of PLLA (48 MPa), which is usually used as biodegradable stent material. Moreover, the tensile modulus of the above composite is 1711 MPa, which is only 34% of PLLA's modulus (4985 MPa). Therefore, novel composites with sufficient tensile strength and better flexibility are obtained as promising cardiovascular stent material. POLYM. ENG. SCI., 2011. © 2011 Society of Plastics Engineers