Preparation of polybenzimidazole/functionalized carbon nanotube nanocomposite films for use as protective coatings
Author(s) -
Zhang Li,
Ni QingQing,
Shiga Akihiko,
Natsuki Toshiaki,
Fu Yaqin
Publication year - 2011
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.21618
Subject(s) - materials science , nanocomposite , thermogravimetric analysis , dynamic mechanical analysis , fourier transform infrared spectroscopy , carbon nanotube , composite material , x ray photoelectron spectroscopy , polymer , raman spectroscopy , transmission electron microscopy , chemical engineering , nanotechnology , physics , optics , engineering
Functionalized multi‐walled carbon nanotubes (MWCNTs) via microwave‐induced polymerization modification route, and polybenzimidazole (PBI) nanocomposite films containing 0.1‐5 wt% functionalized MWCNTs were successfully synthesized. The functionalized MWCNTs were characterized by field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and X‐ray photoelectron spectroscopy (XPS). The results verify that the polymer was successfully grafted to the MWCNTs with a polymer layer that was several nanometers thick. The TGA results showed that the quantity of the attached polymer reached approximately 9.4 wt%. The mechanical properties of the nanocomposite films were measured by tensile test and dynamic mechanical analysis (DMA). The tensile test results indicated that the Young's modulus increased by about 43.9% at 2 wt% CNT loading, and further modulus growth was observed at higher filler loading. The DMA studies indicated that the nanocomposite films had a higher storage modulus than pure PBI film in the temperature range of 30‐300°C, and the storage modulus was maintained above 0.82 GPa. Simulation results confirmed that the PBI nanocomposite films had desirable mechanical properties for use as a protective coating. POLYM. ENG. SCI., 2011. © 2011 Society of Plastics Engineers.