Synthesis, thermal properties, and flame retardance of the epoxy‐silsesquioxane hybrid resins
Author(s) -
Lu Tingli,
Chen Tao,
Liang Guozheng
Publication year - 2007
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.20676
Subject(s) - epoxy , materials science , silsesquioxane , differential scanning calorimetry , curing (chemistry) , diglycidyl ether , thermal stability , glass transition , composite material , polymer chemistry , bisphenol a , chemical engineering , polymer , physics , thermodynamics , engineering
Epoxy/silsesquioxane‐OH (EP‐SDOH, ED) hybrid resins were prepared from cyclohexyl‐disilanol silsesquioxane (SDOH) and diglycidyl ether of bisphenol A via the reaction between silanol and the oxirane group, with the cobalt naphthanate as a catalyst. It was found that incorporation of SDOH allows the reaction between oxirane ring and SiOH, and the silsesquioxane cage structure can be the main chain or as the side chain of the hybrid resin. The EP‐SDOH hybrid resins with various SDOH contents were cured by 4,4′‐diaminodiphenylsulphone, and the curing reaction was investigated by differential scanning calorimetry. The curing characteristics of EP‐SDOH hybrids had been observed to be influenced by the content of SDOH in the hybrid. The differential scanning calorimetry thermograms indicated that the EP‐SDOH hybrid exhibited a higher initial temperature, peak temperature, as well as final temperature than those of the pure epoxy resin when cured by the same curing agent 4,4′‐diaminodiphenylsulphone. The curing kinetic parameters were calculated by using the Ozawa method and the results indicated that EP‐SDOH hybrids possess the same curing mechanism as the pure epoxy resin. The properties of the cured EP‐SDOH hybrid resins such as the glass transition temperature ( T g ), dynamic mechanical analysis, thermal stability, as well as the flame retardance were also investigated, and the results showed that introducing silsesquioxane‐OH unit into epoxy resin successfully modified the local structure, made the chain stiffness, restrict the chain mobility, and eventually improved thermal stability and flame retardance of epoxy resin. POLYM. ENG. SCI., 47:225–234, 2007. © 2007 Society of Plastics Engineers.