Development and characterization of reactively extruded PVC/polystyrene blends
Author(s) -
Haba Y.,
Narkis M.
Publication year - 2004
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.20143
Subject(s) - materials science , polystyrene , composite material , monomer , thermal stability , extrusion , dynamic mechanical analysis , glass transition , polymerization , plasticizer , reactive extrusion , polyvinyl chloride , chemical engineering , polymer chemistry , polymer , engineering
PVC/PS blends are obtained through a reactive extrusion–polymerization method by the absorption of a solution of styrene monomer, initiator, and a crosslinking agent in commercial suspension‐type porous polyvinyl chloride (PVC) particles, forming a dry‐blend with a relatively high monomer content. These PVC/styrene dry‐blends are reactively polymerized in a twin‐screw extruder in the melt state. They do not contain monomer residues as detected by GC. The transparency, fracture surface morphology, thermal stability, rheology and static and dynamic mechanical properties of these blends are compared to physical PVC/PS blends at similar compositions. Owing to the high polymerization temperature (180°C), short PS chains are formed in the reactive extrusion process. These short chains are dispersed both as a separate phase of ∼2 μm particles (recognized by SEM) and also as molecularly dispersed chains enhancing plasticization and compatibilization. The molecularly dispersed short PS chains tend to plasticize the PVC phase, reducing its melt viscosity and glass transition temperature. The content of the short PS chains forming the dispersed separate PS particles is too low for DMTA to detect a separate T g . Thus, reactively extruded PVC/PS blends exhibit single T g transitions at lower temperatures compared with the neat PVC. Migration of the PVC's low‐molecular‐weight additives (lubricants and thermal stabilizer) to the PS phase is observed in the physical PVC/PS blends, causing antiplasticization of the PS phase. This results in both reduction of the T g and an increase in the thermal stability of the PS phase in the physical PVC/PS blends. Comparing TGA thermograms of reactively extruded and physical PVC/PS indicates that the PS formed in the extruder is different from the commercial PS. This can stem from various chemical reactions that can take place in the studied reactive polymerization process. Polym. Eng. Sci. 44:1473–1483, 2004. © 2004 Society of Plastics Engineers.