Reinforcement of polyamide 6 with thermotropic liquid crystalline polymer
Author(s) -
Kurokawa M.,
Nagai S.
Publication year - 1999
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.11476
Subject(s) - materials science , composite material , softening point , polyamide , extrusion , epoxy , polymer , copolyester , thermotropic crystal , composite number , liquid crystalline , polyester
The in‐situ composites of polyamide 6 (PA 6)/liquid crystalline polymer (LCP) were investigated from the standpoint of fibrillation of LCP to develop a new high performance gear material for heavy load use that is superior to conventional plastic gears made of polyacetal (POM). LCP used was a wholly aromatic copolyester. PA 6 was chosen as the matrix polymer because of its excellent fatigue resistance. Extrusion of PA 6 added with LCP from 10 to 30 vol% was carried out at a temperature between 260 and 290°C by a twin screw extruder and take‐up equipment. Insitu fibrillation of LCP droplets, which were dispersed in PA 6 matrix, took place during the process. Injection molding of the composites was followed at a temperature below the softening point of LCP fibrils so as to keep the fibrils as extruded. Key factors for fibrillation of LCP were found as follows: (1) control of stress relaxation of LCP when the melt passes through the die‐head, (2) the optimum temperature of nent, (3) the optimum LCP content, and (4) addition of a small amount of 3rd component. A gear made of in‐situ composite of PA 6/LCP (30 vol%) added with 2‐functional epoxy resin (2.5 phr) was found to bear a load about 1.2 times heavier than a POM gear.