Stress‐initiated void formation during cure of a three‐dimensionally constrained thermoset resin
Author(s) -
Eom Yongsung,
Boogh Louis,
Michaud Véronique,
Sunderland Paul,
Månson JanAnders
Publication year - 2001
Publication title -
polymer engineering and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.503
H-Index - 111
eISSN - 1548-2634
pISSN - 0032-3888
DOI - 10.1002/pen.10746
Subject(s) - materials science , thermosetting polymer , void (composites) , composite material , shrinkage , epoxy , curing (chemistry) , viscoelasticity , mold , isothermal process , composite number , ultimate tensile strength , modulus , physics , thermodynamics
Abstract During cure of epoxy resins, polymerization induces an increase in mechanical properties, which is accompanied by a volumetric shrinkage. When the resin is cured in a constrained mold to which it adheres, tensile stresses will hence develop, which may exceed the stremgth of the resin at a given curing stage. Voids will then form. The origin and governing parameters of void formation are studied using an epoxy resin cured in a three‐dimensionally constrained glass mold following isothermal cure cycles. Two types of voids are shown to appear during cure, one early in the process and a second around the gelation point. A viscoelastic analysis of the material stress state over the whole range of cure is performed. Both the viscoelastic modulus obtained from a time‐cure‐temperature superposition and the volumetric shrinkage, which was continuously measured by density change, are taken into account. A value for the critical internal stress at void initiation is thus proposed. This criterion can be used to provide guidelines for tailoring the material properties toward an increase of the critical stress for void initiation. Also, since during theprocessing of composite materials, cases may arise where the resin cures within the interstices left between consolidated fibres that do not move, this critical stress failure criterion can be of use in the eastablishment of a process window providing guidelines for the production of void free composites.