Dynamic mechanical property and interlaminar shear strength of the carbon fabric reinforced polyetherimide composite based on the polyetherimide resin films
Author(s) -
Tan Zhongyang,
Wang Jun,
Ma Yanqiong,
Wang Daming,
Zhao Xiaogang,
Chen Chunhai
Publication year - 2017
Publication title -
polymer composites
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.577
H-Index - 82
eISSN - 1548-0569
pISSN - 0272-8397
DOI - 10.1002/pc.23625
Subject(s) - polyetherimide , materials science , composite material , dynamic mechanical analysis , nitric acid , composite number , composite laminates , modulus , polymer , metallurgy
In this study, the laminates reinforced with the concentrated nitric acid or acetone treated carbon fabrics were prepared based on polyetherimide films with different thickness including 30 μm and 50 μm, respectively. 4 Harness Satin (4HS) and 5 Harness Satin (5HS) carbon fabrics were used as the reinforcements of the composite laminates. Three impact factors, including the polyetherimide film thickness, fabric treatment method and fabric type, were considered in this study. Interlaminar shear strength (ILSS) measurement shown that the thicker polyetherimide film (50 μm), 4HS carbon fabric and the nitric acid treatment of the fabric could be used to increase the ILSS value because of the improvement of the interfacial property for the laminate. The 50 μm thickness polyetherimide films used in the laminates improved the storage modulus, and decreased the glass transition temperatures ( T g s) by DMA or DSC. It was because that the better interfacial property and the stronger mobility of the polymer chain under the greater residual internal stress in the laminate was obtained with the increase of the polyetherimide film thickness. The nitric acid treatment of the fabric increased the T g s measured by DMA and DSC, and decreased the tan δ peak values of the laminates because of the stronger interfacial adhesion between the fiber and the resin and the decreased mobility of the polymer chain. In addition, the effects of above three impact factors on the ILSS, storage modulus, loss modulus, tan δ and the T g of the laminate were discussed in detail by ILSS, DMA and DSC measurement, respectively. POLYM. COMPOS., 38:663–672, 2017. © 2015 Society of Plastics Engineers