Preparation of nanocomposites by melt compounding polylactic acid/polyamide 12/organoclay at different screw rotating speeds using a twin screw extruder
Author(s) -
Hasook Aniwat,
Muramatsu Hiroki,
Tanoue Shuichi,
Iemoto Yoshiyuki,
Unryu Tsunemune
Publication year - 2008
Publication title -
polymer composites
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.577
H-Index - 82
eISSN - 1548-0569
pISSN - 0272-8397
DOI - 10.1002/pc.20336
Subject(s) - organoclay , materials science , nanocomposite , compounding , ultimate tensile strength , composite material , polylactic acid , polyamide , plastics extrusion , thermal stability , dynamic mechanical analysis , polymer , chemical engineering , engineering
This study analyzes the effect of different screw rotating speeds on the clay dispersion and mechanical properties of nanocomposites prepared by melt compounding polylactic acid (PLA) with an organoclay in a co‐rotating twin screw extruder. Polyamide 12 (PA12) was used as an additive. Two different screw rotating speeds, 65 rpm and 150 rpm, were used in this study. According to the tensile strength data, the Young's modulus of the PLA/clay nanocomposites showed improvement at a screw rotating speed of 150 rpm. The Young's modulus improved with the addition of the organoclay to PLA matrix, but decreased when PA12 was added to the PLA matrix. The tensile strengths and elongations become small by adding organoclay to PLA matrix. The tensile strengths of the PLA/organoclay nanocomposites increased for the higher screw rotating speed (150 rpm). The d ‐spacing of PLA/PA12/Clay nanocomposites was independent of the addition of PA12. The size of the clay aggregates in the PLA/PA12/Clay nanocomposites is smaller than that of PLA/Clay. Furthermore, the thermal stability of the PLA/Clay nanocomposite increases with addition of PA12, while on the whole, it had little influence on the tensile properties. POLYM. COMPOS., 29:1–8, 2008. © 2007 Society of Plastics Engineers