Production of leather‐like composites using short leather fibers. II. Mechanical characterization
Author(s) -
MaderaSantana T. J.,
AguilarVega M. J.,
Márquez A.,
Vázquez Moreno F.,
Richardson M. O. W.,
Cruz Machin J. L.
Publication year - 2002
Publication title -
polymer composites
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.577
H-Index - 82
eISSN - 1548-0569
pISSN - 0272-8397
DOI - 10.1002/pc.10495
Subject(s) - materials science , composite material , ultimate tensile strength , scanning electron microscope , fiber , composite number , compatibilization , polyamide , polymer , polymer blend , copolymer
Leather‐like composites were prepared by addition of chemically modified short leather fibers (SLF) into a plasticized polyvinyl chloride (pPVC) matrix. The fibers were subjected to chemical modification by emulsion polymerization to achieve good interfacial adhesion between SLF and the pPVC matrix. The SLF with chemical modification were obtained from three different reaction conditions where these SLF have different percentages of grafted and deposited PMMA polymer onto the fiber surface. The incorporation of the SLF into the thermoplastic matrix was carried out using a torque‐rheometer and the composites obtained were molded by compression. Tensile and tear mechanical tests were performed on composite samples, and the morphology of the fractured surfaces was analyzed using scanning electron microscopy (SEM). The results show that the incorporation by grafting of polymethyl metacrylate (PMMA) onto the fibers produced a significant improvement of their interfacial adhesion to pPVC, promoting the compatibilization between the fiber surface and matrix. The findings are discussed and interpreted in terms of enhanced adhesion at phase boundaries. Overall, the results confirm that it is possible to produce modified leather composites based on a pPVC matrix, which exhibit relatively high tensile strength, tear resistance and flexibility. These composites are very suitable candidate materials for applications in the footwear industry.