Thermal degradation and flame retardancy of fumaric acid in thermoplastic polyurethane elastomer
Author(s) -
Wei Zhibiao,
Chen Xilei,
Jiao Chuanmei
Publication year - 2019
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.4462
Subject(s) - limiting oxygen index , cone calorimeter , thermoplastic polyurethane , materials science , fire retardant , thermogravimetric analysis , char , composite material , fourier transform infrared spectroscopy , elastomer , combustion , nuclear chemistry , chemical engineering , organic chemistry , chemistry , engineering
In this paper, fumaric acid (FA) which was a new type of environmental and low‐cost flame retardant was applied for thermoplastic polyurethane elastomer (TPU). The flame‐retardant properties of TPU were tested using limiting oxygen index, cone calorimeter test, smoke density test, and thermogravimetric/Fourier transform infrared spectroscopy. It has been proved that FA could improve the difficulty of the ignition of the sample; the limiting oxygen index value of the sample (FA‐4) increased by 29.7% when 2.0 wt% FA was added to TPU. The cone calorimeter test showed that FA can greatly reduce heat release and smoke production during the combustion process of TPU composites. For example, compared with the pure TPU, the peak heat release rate and total smoke release of the sample (FA‐4) with 2.0 wt% FA were decreased by 50.8% and 51.5% respectively. The results of smoke density test showed that the luminous flux of the samples contained 0.5 wt% FA was increased by 79.2% compared with the pure TPU. The TG results revealed that the sample of FA‐4 had higher char residue content compared with the sample of TPU. The results of thermogravimetric/Fourier transform infrared spectroscopy proved that FA could decrease the initial decomposition temperature for TPU composites and increase the release of CO 2 and H 2 O. All results of test illustrated that FA had good flame‐retardant effect on TPU.