Sodium alginate/magnesium oxide nanocomposite scaffolds for bone tissue engineering
Author(s) -
NasriNasrabadi Bijan,
Kaynak Akif,
Heidarian Pejman,
KomeilyNia Zahra,
Mehrasa Mohammad,
Salehi Hossein,
Kouzani Abbas Z.
Publication year - 2018
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.4367
Subject(s) - materials science , leaching (pedology) , nanocomposite , chondrocyte , sodium alginate , nuclear chemistry , chitosan , tissue engineering , nanoparticle , sodium , chemical engineering , magnesium , scaffold , composite material , biomedical engineering , nanotechnology , in vitro , chemistry , metallurgy , biochemistry , medicine , environmental science , soil science , engineering , soil water
A simple 2‐step method, consisting of film casting and polyvinyl alcohol leaching, is proposed to prepare magnesium oxide (MO) nanoparticle‐reinforced sodium alginate scaffolds with right properties for bone tissue engineering. The cytocompatibility of the as‐prepared scaffolds was also evaluated using the 3‐(4,5‐dimethylthiazol‐2‐yl)‐2,5‐diphenyltetrazolium‐bromide yellow tetrazole assay test, wherein chondrocyte cells had been considered as target cells. According to the results, the ensuing sodium alginate nanocomposites, containing 4‐wt% MO nanoparticles, demonstrated the highest physical and mechanical properties after leaching step. The Young modulus of sodium alginate/4‐wt% MO was improved about 44%, in comparison with that of the pure alginate sample. Furthermore, incorporating MO nanoparticles up to 4 wt% controlled the liquid uptake capacity of scaffolds vis‐à‐vis the resultant pure sodium alginate sample. Moreover, with increasing the nanoparticle content, the antibacterial properties of scaffolds enhanced, but their degradation rates under in vitro conditions tapered off. With the introduction of 3‐ and 4‐wt% MO, the average diameter of the bacterial zone of the scaffold samples reduced to less than 10 mm 2 , suggesting an insensitive antimicrobial performance, compared with the pure sodium alginate and the samples with 1‐ and 2‐wt% MO content, which exhibit antimicrobial sensitivity. 3‐(4,5‐Dimethylthiazol‐2‐yl)‐2,5‐diphenyltetrazolium‐bromide assay test also revealed the cultivated chondrocyte cells on the 4‐wt% MO nanoparticle‐reinforced scaffold possessed better interaction as well as appropriate cell attachment and proliferation than the pristine sodium alginate sample.