Comparative mechanical property characterization of three indirect composite resin materials compared with two direct composites
Author(s) -
Demirel Figen,
Saygılı Gülbin,
Şahmalı Sevil
Publication year - 2003
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.344
Subject(s) - flexural strength , materials science , composite material , fracture toughness , vickers hardness test , composite number , indentation hardness , izod impact strength test , bending , toughness , microstructure , ultimate tensile strength
Various new indirect composite materials have been developed with required advantages. In this study three indirect composite material (Artglass, Belleglass HP, Targis) were tested for flexural strength, fracture toughness, wear resistance and hardness against Filtek P60 and Z‐100. Five specimens of each material were fabricated according to the manufacturer's directions. The flexural strength and fracture toughness was measured using the bending test. The wear test was performed to accelerated wear in a toothbrushing apparatus. Vickers hardness was measured for each of the tested materials. The statistical tests used for flexural strength, fracture toughness, wear and hardness were One‐way ANOVA and Kruskal–Wallis test. The level of statistical significance chosen was p  = 0.05. Results of the study showed that Filtek P60 was superior to the other composites in all tests. Significant differences were found among the materials. The differences in flexural strength, fracture toughnes, wear and hardness may have been due to differences in chemistry or method of polymerization of the composites. Copyright © 2003 John Wiley & Sons, Ltd.