Synthesis and properties of thermally stable polyimides bearing pendent fluorene moieties
Author(s) -
Rafiee Zahra,
Golriz Leila
Publication year - 2014
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.3396
Subject(s) - fluorene , diamine , monomer , polymer chemistry , materials science , polymer , polymerization , condensation polymer , glass transition , composite material
A new diamine monomer containing fluorene unit, 3,5‐diamino‐ N ‐(9H‐fluoren‐2‐yl)benzamide was successfully synthesized via the condensation of 2‐aminofluorene and 3,5‐dinitrobenzoyl chloride and subsequent reduction of the dinitro compound. A series of novel aromatic polyimides having pendent fluorenamide moieties were prepared from the reaction of the diamine monomer and various tetracarboxylic dianhydrides by a conventional two‐step polymerization process. The polyimides were obtained in quantitative yields with inherent viscosities of 0.33–0.44 dl/g. The resulting polymers dissolved in N ‐methyl‐2‐pyrrolidinone, N , N ‐dimethylacetamide, N , N ‐dimethylformamide, and dimethyl sulfoxide. The glass transition temperature of these polymers was in the range of 261–289°C. They were fairly stable up to a temperature around 450°C and lost 10% weight in the range of 498–556°C in nitrogen. The UV–vis absorption spectra showed that all of the polymers had absorption maxima around 320 nm. Cyclic voltammograms of the polyimides revealed an oxidation wave with a peak around 1.3 V. Copyright © 2014 John Wiley & Sons, Ltd.