UV‐curable acrylate‐based nanocomposites: effect of polyaniline additives on the curing performance
Author(s) -
Jafarzadeh Shadi,
Johansson Mats,
Sundell PerErik,
Claudino Mauro,
Pan Jinshan,
Claesson Per M.
Publication year - 2013
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.3131
Subject(s) - polyaniline , materials science , acrylate , curing (chemistry) , fourier transform infrared spectroscopy , nanocomposite , uv curing , polymerization , chemical engineering , composite material , ultraviolet , polymer chemistry , polymer , copolymer , engineering , optoelectronics
Composites of nanostructured polyaniline (PANI) conducting polymer in a polyester acrylate (PEA) formulation were made to provide conductive organic coatings. The effect of the presence and amount of PANI on the photocuring performance of the ultraviolet (UV)‐curable acrylate system has been investigated employing real‐time Fourier transform infrared spectroscopy as the main technique. Longer initial retardation of the radical polymerization and lower rates of cross‐linking reactions were observed for dispersions containing PANI of higher than 3wt.%. The PEA/PANI samples were more affected than the neat PEA resin by the changes in UV light intensity and oxygen accessibility during UV curing. Samples with higher PANI content, of up to 10wt.%, were tested and could be partially cured even at UV light intensities as low as 2 mW cm −2 when the oxygen replenishment into the system was inhibited. Thermal analysis revealed that the presence of PANI did not induce any significant change in Tg of the cured system, meaning that early decrease in mobility and vitrification is not the reason for lower ultimate conversion of the dispersions with higher PANI content compared with the neat PEA resin. Curing under strong UV lamps, of 1.5 W cm −2 intensity, made it possible to reach high degrees of conversion on films with similar mechanical properties independent of the PANI content. Copyright © 2013 John Wiley & Sons, Ltd.