Electrical resistance and heat generation of polypyrrole‐coated polyacrylonitrile nanofibrous and regular fibrous mats
Author(s) -
Oroumei Azam,
Tavanai Hossein,
Morshed Mohammad
Publication year - 2012
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.2049
Subject(s) - polypyrrole , polyacrylonitrile , materials science , composite material , electrical resistivity and conductivity , fiber , electrical resistance and conductance , electrospinning , conductive polymer , polymer , polymerization , electrical engineering , engineering
This article reports the effect of fiber diameter on the electrical resistance and heat generation of fibrous polyacrylonitrile (PAN) mats coated with polypyrrole during chemical in situ polymerization. Polypyrrole is one of the important intrinsically conducting polymers that perform similar to semiconductors. The electrical resistance of polypyrrole‐coated mats depends on the fiber diameter, the applied pressure on the surface of the mats, and the mat thickness. The electrical resistance of polypyrrole‐coated PAN fibrous mats decreases as fiber diameter decreases. Moreover, electrical resistance decreases considerably as the mat thickness as well as the applied pressure on it increases. It was also observed that the heat generated in polypyrrole‐coated PAN fibrous mats increases with voltage and duration of the applied voltage. Lower fiber diameter also leads to higher heat generation. Furthermore, electrical current increases rapidly in the initial stages of applying voltage and then shows a marginal increase. Considering their high specific surface area, nanofibers convey considerable improvement in the electrical conductivity as well as heat generation capacity of the mats made from them. Copyright © 2011 John Wiley & Sons, Ltd.