Polyethersulfone/polyacrylonitrile blend ultrafiltration membranes with different molecular weight of polyethylene glycol: preparation, morphology and antifouling properties
Author(s) -
Amirilargani Mohammad,
Sabetghadam Anahid,
Mohammadi Toraj
Publication year - 2012
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.1888
Subject(s) - polyacrylonitrile , membrane , materials science , polyethylene glycol , ultrafiltration (renal) , chemical engineering , phase inversion , casting , peg ratio , polymer chemistry , solvent , dimethylformamide , biofouling , polymer , chromatography , composite material , chemistry , organic chemistry , finance , engineering , economics , biochemistry
Asymmetric ultrafiltration (UF) membranes were prepared from blends of polyethersulfone (PES)/polyacrylonitrile (PAN) via phase inversion method induced by immersion precipitation. Polyethylene glycol (PEG) with four different molecular weights was used as pore former and hydrophilic polymeric additive. N , N ‐dimethylformamide (DMF) and water were used as solvent and coagulant (nonsolvent), respectively. The effects of different proportion of PES/PAN and molecular weight of PEG on morphology and performance of the prepared membranes were investigated. Performance of the membranes was evaluated using UF experiments of pure water and buffered bovine serum albumin (BSA) solution as feed. The contact angle measurements indicated that the hydrophilicities of PES/PAN membrane increase by increasing the PAN concentration in the casting solution. However, performance of the membranes improves by increasing the PAN concentration in the casting solution up to 20% and then decreases with further addition of PAN. It was found out that the rejection of BSA decreases with increasing the PAN concentration in the casting solution. Furthermore, it was found that the performance of the membranes increases by increasing the molecular weight of PEG up to 1500 Da and then decreases with the higher molecular weights. The morphology of the prepared membranes was studied by scanning electron microscopy. Copyright © 2011 John Wiley & Sons, Ltd.