Premium
The role of interfacial compatibilization upon the microstructure and electrical conductivity threshold in polypropylene/expanded graphite nanocomposites
Author(s) -
Mirzazadeh Hossein,
Katbab Ali A.,
Hrymak Andrew N.
Publication year - 2011
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.1589
Subject(s) - materials science , polypropylene , nanocomposite , differential scanning calorimetry , composite material , scanning electron microscope , thermogravimetric analysis , compatibilization , maleic anhydride , conductivity , microstructure , graphite , dispersion (optics) , polymer blend , chemical engineering , polymer , copolymer , chemistry , physics , engineering , thermodynamics , optics
Abstract Attempts have been made to evaluate the effect of interface and degree of interfacial interaction upon electrical conductivity threshold in polypropylene/expanded graphite (PP/EG) nanocomposites, and dispersion state of graphite nanosheets. For this purpose, maleic anhydride grafted polypropylene (PPgMA) and maleic anhydride grafted EPDM (EPDMgMA) were used as compatibilizer. Nanocomposite samples containing 1–5 vol% of EG were prepared by melt mixing method using laboratory scale internal mixer. Characterization was carried out by using X‐ray diffraction (XRD), differential scanning calorimeter (DSC), thermo‐gravimetric analysis (TGA), scanning electron microscope (SEM), transmission electron microscope (TEM), and rheo‐mechanical spectroscopy (RMS). The conductivity measurements were carried out by using four point probe method according to ASTM D991. Results showed that the conductivity threshold is controlled by the extent of interfacial interaction between PP and EG. So, better conductivity was obtained using PPgMA as compatibilizer which causes higher level of interaction between PP and EG, and therefore better dispersion of the EG nanolayers in the polymer matrix. On the other hand, high levels of compatibilizers, especially EPDMgMA, caused formation of separated aggregates of EG shelled with the compatibilizer, which results in the reduction of conductivity of the nanocomposites. This finding has been verified by SEM, RMS, and conductivity measurements. Effects of EG nanolayers on crystalline structure and thermal decomposition temperature of the nanocomposites have also been investigated by DSC and TGA, respectively. Copyright © 2009 John Wiley & Sons, Ltd.