Characteristics of paint systems prepared from dammar with the addition of natural pigment
Author(s) -
Omar N. M.,
Ahmad A. H.
Publication year - 2009
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.1247
Subject(s) - materials science , corrosion , composite material , viscometer , coating , dielectric spectroscopy , adhesion , paint adhesion testing , electrochemistry , chemical engineering , viscosity , electrode , chemistry , engineering
Adhesion and electrochemical properties of paint system prepared from dammar binder or binder from Dipterocarpus grandifolius with the addition of natural pigment have been investigated. In this work, carotenoid pigment obtained from Capsicum annum (dried chili pepper) was added into the mixture of dammar resin and acrylic polyol resin to form the organic paint system. Five different paint systems were formulated on the basis of various concentrations of dammar resin, and their viscosities were measured by using Brookefield Viscometer. The paint systems were proofed on Aluminum steel Q‐panels as a substrate. The cured paint systems were then evaluated by using the crosshatch adhesion method to test their adhesion properties according to ASTM D3359 standards. The corrosion potential property of paint was characterized by using electrochemical impedance spectroscopy (EIS) while the coated substrate was exposed to 3% NaCl for 30 days. Comparative results have been presented in terms of number of damage grids for the crosshatch test in each sample at different viscosity conditions and also regarding the ability of the coated sample to resist the corrosion potential. The result shows that the paint system with a composition of 35% dammar (CD35%) possessed the best adhesion performance compared to other CD paint compositions. Furthermore, CD35% also had higher corrosion resistance after 30 days of exposure in the 3% NaCl solution. The decrease in coating resistance values is associated with the electrolyte penetration into the coating system. The results showed that the developed organic paint system prepared from dammar improved the adhesion and electrochemical properties of a paint system. Addition of natural pigment to the formulation may enhance the attractiveness and vibrancy of the color. Copyright © 2009 John Wiley & Sons, Ltd.