Mechanical characteristics of hydrogenated natural rubber vulcanizates
Author(s) -
Ikeda Yuko,
Phinyocheep Pranee,
Kittipoom Sumet,
Ruancharoen Jareerat,
Kokubo Yota,
Morita Yuichi,
Hijikata Kensuke,
Kohjiya Shinzo
Publication year - 2008
Publication title -
polymers for advanced technologies
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.61
H-Index - 90
eISSN - 1099-1581
pISSN - 1042-7147
DOI - 10.1002/pat.1176
Subject(s) - materials science , natural rubber , glass transition , differential scanning calorimetry , ultimate tensile strength , composite material , modulus , crystallization , thermal stability , vulcanization , polymer , dynamic mechanical analysis , polymer chemistry , chemical engineering , physics , engineering , thermodynamics
Mechanical properties of partially hydrogenated natural rubber (HNR) vulcanizates were evaluated regarding their chemical structure and crystallizable nature of HNR, and are reported here, to the best of our knowledge, for the first time. HNRs of three levels of hydrogenation (20.6, 29.0, and 40.6 mol%) were successfully prepared by the chemical modification of natural rubber (NR) latex using N 2 H 4 and H 2 O 2 as reagents, in a sufficient amount for preparing sulfur‐crosslinked samples to be subjected to mechanical and structural measurements. The three HNR vulcanizates were found to be crystallizable upon stretching; it is noted that even 40.6 mol% hydrogenation did not prevent HNR vulcanizates from crystallization upon stretching, while their onset strain of crystallization was higher than that of NR vulcanizate. The hysteresis loss and residual strain up to a stretching ratio of 2 for the HNR vulcanizates tended to become larger with the increase in the degree of the hydrogenation. Tensile and dynamic mechanical properties of 20.6 mol% hydrogenated HNR vulcanizate were comparable to those of NR vulcanizate. From differential scanning calorimetry and temperature dispersion of dynamic modulus or loss, the glass transition temperatures of HNR vulcanizates were found to be almost the same as that of NR vulcanizate, which is also notable. The thermal stability of HNR vulcanizates was better than that of NR vulcanizate. Thus, this chemical modification seems to give a promising NR derivative whose properties can be equivalent or even better than the mother polymer. Copyright © 2008 John Wiley & Sons, Ltd.