Experimental and Modeling Investigation of Radical Homopolymerization of 2‐(Methacryloyloxyethyl) Trimethylammonium Chloride in Aqueous Solution
Author(s) -
Ezenwajiaku Ikenna H.,
Chovancová Anna,
Lister Kyle C.,
Lacík Igor,
Hutchinson Robin A.
Publication year - 2020
Publication title -
macromolecular reaction engineering
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.37
H-Index - 32
eISSN - 1862-8338
pISSN - 1862-832X
DOI - 10.1002/mren.201900033
Subject(s) - monomer , chemistry , polymerization , polymer chemistry , aqueous solution , kinetics , radical polymerization , chloride , polymer , ionic strength , molar mass , chemical engineering , organic chemistry , physics , quantum mechanics , engineering
The radical homopolymerization kinetics of 2‐(methacryloyloxyethyl) trimethylammonium chloride (TMAEMC) in aqueous solution is investigated across a wide range of initial monomer contents (5–35 wt%), ionic strengths, and pH levels using an in‐situ NMR technique to track monomer consumption over the complete conversion range. Molar mass distributions (MMD) of the final homopolymers are also examined, with additional batch and semi‐batch experiments conducted in a stirred vessel. The rates of monomer conversion and polymer MMDs are dependent on initial monomer content but almost entirely independent of pH and the presence of salts, with some acceleration of rate observed for low monomer levels at very high salt concentration. To aid with the interpretation of these results, the conductivity and counterion activity of monomer and polymer mixtures are measured to determine the extent of electrostatic interactions at various levels of conversion. These results are combined with recently reported measurements of TMAEMC homopropagation kinetics to develop a TMAEMC homopolymerization model that captures the systematic decrease in rates of monomer conversion observed with increased initial monomer content during batch polymerization as well as provides a good representation of semi‐batch polymerization.