Auswirkung der Bindungstemperatur auf das Gefüge und die Bildung intermetallischer Verbindungen bei diffusionsgebundenen Magnesium/Aluminium‐Verbindungen
Author(s) -
Mofid M.A.,
Loryaei E.
Publication year - 2020
Publication title -
materialwissenschaft und werkstofftechnik
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.285
H-Index - 38
eISSN - 1521-4052
pISSN - 0933-5137
DOI - 10.1002/mawe.201900080
Subject(s) - intermetallic , liquation , microstructure , eutectic system , diffusion bonding , materials science , metallurgy , thermocompression bonding , magnesium , diffusion welding , grain boundary , aluminium , welding , diffusion , atomic diffusion , crystallography , composite material , chemistry , alloy , thermodynamics , physics , layer (electronics)
The diffusion bonding of two dissimilar alloys Aluminum 5083 and Magnesium AZ31 was carried out at 420 °C, 430 °C,440 °C and 450 °C for bonding time of 60 min. In order to characterize the microstructure evolution in the joint zone, scanning electron microscopy, energy dispersive spectroscopy and x‐ray diffraction were applied. The results show that joint formation is attributed to the solid‐state diffusion of magnesium and aluminum into Aluminum 5083 and Magnesium AZ31 alloys followed by eutectic formation and constitutional liquation along the interface. At bonding temperature of 430 °C diffusion induced grain coarsening was observed at the interface. With increase in bonding temperature, the atomic diffusivity increases, results in easier and speeder chemical bonding. In bonding temperature of 440 °C the weld had an irregular shaped region in the weld center, having a different microstructure from the two base materials. The irregular shaped region contained a large volume of intermetallic compound Al 12 Mg 17 and showed significantly higher hardness in the weld center. The present study suggests that constitutional liquation resulted in the intermetallic compound Al 12 Mg 17 in the weld center.