Deposition and corrosion behavior of silicate conversion coatings on aluminum alloy 2024
Author(s) -
Kazemi M.,
Danaee I.,
Zaarei D.
Publication year - 2014
Publication title -
materialwissenschaft und werkstofftechnik
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.285
H-Index - 38
eISSN - 1521-4052
pISSN - 0933-5137
DOI - 10.1002/mawe.201400212
Subject(s) - potassium silicate , silicate , conversion coating , corrosion , dielectric spectroscopy , materials science , coating , alloy , polarization (electrochemistry) , aluminium , metallurgy , chemical engineering , electrochemistry , sodium silicate , composite material , chemistry , electrode , engineering
Potassium silicate was deposited on AA2024 aluminum alloy as environmentally friendly conversion coatings and its corrosion behavior were examined by means of electrochemical impedance spectroscopy, potentiodynamic polarization and surfaces techniques. Potentiodynamic polarization curves show significant decrease in corrosion current density of silicate coated aluminum in NaCl solution. The corrosion resistance was increased with increasing silicate concentration of coating baths. The results indicated that the coating applied from 3 molar silicate baths is more uniform and continuous. The X‐ray diffraction (XRD) and energy discharge spectroscopy (EDS) spectra confirm the existence of silicate film on the AA2024 surface. The coating performance was evaluated in acidic and basic NaCl solution and the results show the stability of silicate conversion coating in these solutions.