Die kontrollierte Reduktion von Palladium Nanopartikeln auf der Oberfläche von chemisch modifizierten Silicaten
Author(s) -
Ivashchenko N.,
Tertykh V.,
Yanishpolskii V.,
Khainakov S.,
Dikhtiarenko A.
Publication year - 2011
Publication title -
materialwissenschaft und werkstofftechnik
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.285
H-Index - 38
eISSN - 1521-4052
pISSN - 0933-5137
DOI - 10.1002/mawe.201100733
Subject(s) - palladium , nuclear chemistry , nanocomposite , transmission electron microscopy , materials science , scanning electron microscope , mesoporous silica , chemistry , nanoparticle , metal , mesoporous material , infrared spectroscopy , polymer chemistry , nanotechnology , catalysis , metallurgy , organic chemistry , composite material
The reduction of palladium ions by silicon hydride groups grafted to the surface of silica matrices was applied for the synthesis of palladium‐containing nanocomposites. Ordered mesoporous silicas, such as MCM‐41 and SBA‐15, along with silochrom type silica were used as supports for palladium nanoparticles in order to obtain encapsulated in pores metal particles. The synthesized nanocomposites have been studied by IR‐spectroscopy, X‐ray diffraction analysis, low‐temperature nitrogen adsorption and transmission electron microscopy. Die Reduktion von Palladiumionen durch Siliciumhydrid‐Gruppen an der Oberfläche einer Silikatmatrix wurde für die Synthese von Palladium‐haltigen Nanokompositen eingesetzt. Geordnete mesoporöse Silikate wie MCM‐41 oder SBA‐15 wurden gemeinsam mit silochromen Silikattypen als Träger für die Palladiumnanopartikel genutzt, um sie in Metallporen einzuschließen. Die synthetisierten Nanopartikel wurden mit IR‐Spektroskopie, Röntgenbeugung, Tieftemperaturstickstoffadsorption und Transmissionselektronen‐Mikroskopie untersucht.