Preparation and Properties of Polystyrene/SEBS Blends with Compositional Gradients in Their Sheet Direction
Author(s) -
Agari Yasuyuki,
Yamamoto Taichi,
Nomura Ryoki
Publication year - 2006
Publication title -
macromolecular symposia
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.257
H-Index - 76
eISSN - 1521-3900
pISSN - 1022-1360
DOI - 10.1002/masy.200651001
Subject(s) - elongation , materials science , polystyrene , composite material , copolymer , polymer blend , styrene , diffusion , polymer , ultimate tensile strength , thermodynamics , physics
There have been a few reports that discussed polymer blends with compositional gradient in their sheet directions. Thus, we discussed the preparation of the graded polystyrene(PS)/styrene‐hydorogenated butadiene‐ styrene block copolymer(SEBS) blend with compositional gradient in their sheet directions, by applying of the solution‐diffusion method. Then, the hardness on the air side surface of the graded blend gradually increased with shifting the measured point from the edge containing lowest PS content. All of the areas, into which the graded blend sheet was divided, were almost equal in length, when total elongation was 6.6 mm. However, the length of the area became longer at the larger SEBS content, when the total elongation was 175 mm. The ratio of the length of the area to that in lowest SEBS content increased gradually with increasing of SEBS content, when the total elongation became over 50 mm. It was considered that this phenomenon occurred, because of the compositional gradient in the PS/SEBS graded blend.