Thermal and Surface Properties of Phenolic Nanocomposites Containing Octaphenol Polyhedral Oligomeric Silsesquioxane
Author(s) -
Lin HanChing,
Kuo ShiaoWei,
Huang ChihFeng,
Chang FengChih
Publication year - 2006
Publication title -
macromolecular rapid communications
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 1.348
H-Index - 154
eISSN - 1521-3927
pISSN - 1022-1336
DOI - 10.1002/marc.200500852
Subject(s) - silsesquioxane , nanocomposite , contact angle , glass transition , materials science , polymer chemistry , chemical engineering , x ray photoelectron spectroscopy , thermal stability , phenol , polymer , chemistry , organic chemistry , composite material , engineering
Summary: We have synthesized a new polyhedral oligomeric silsesquioxane (POSS) containing eight phenol functional groups and copolymerized it with phenol and formaldehyde to form novolac‐type phenolic/POSS nanocomposites exhibiting high thermal stabilities and low surface energies. Our DSC results indicate that the glass transition temperature of these nanocomposites increased initially upon increasing their POSS content, but then decreased at POSS content above 10 wt.‐%, presumably because of the formation of relatively low molecular weight species and POSS aggregation as evidenced from MALDI‐TOF mass analyses. Our TGA analyses indicated that the 5‐wt.‐%‐mass‐loss temperatures ( T d ) increased significantly upon increasing the POSS content because the incorporation of the POSS led to the formation of an inorganic protection layer on the nanocomposite's surface. XPS and contact angle data provided positive evidence to back up this hypothesis. In addition, contact angle measurements indicated a significant enhancement in surface hydrophobicity after increasing the POSS content.Syntheses procedures of phenolic/OP‐POSS nanocomposites.