On the Use of Surfactant‐Complexed Chitosan for Toughening 3D Printed Polymethacrylate Composites
Author(s) -
Maalihan Reymark D.,
Chen Qiyi,
Agueda Joseph Rey H. Sta.,
Pajarito Bryan B.,
Tamura Hiroshi,
Advincula Rigoberto C.
Publication year - 2021
Publication title -
macromolecular materials and engineering
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.913
H-Index - 96
eISSN - 1439-2054
pISSN - 1438-7492
DOI - 10.1002/mame.202000448
Subject(s) - materials science , ultimate tensile strength , composite material , toughness , composite number , pulmonary surfactant , nanocomposite , chitosan , chemical engineering , engineering
This work reports a simple approach to prepare toughened 3D‐printed polymethacrylate (PMA) composites using surfactant‐modified chitosan (SMCS) particles at loadings between 2–10 wt%. Chitosan (CS) is modified with anionic surfactant, sodium dodecyl sulfate, via ionic complexation to facilitate compatibility and dispersion of CS to PMA matrix by non‐covalent interactions between the components. The study successfully demonstrates high‐accuracy 3D printing of composites with significant improvements in the overall mechanical properties. The composite with the best loading of 8 wt% SMCS shows a tensile modulus of 1.23 ± 0.05 GPa, a tensile strength at 49.8 ± 0.96 MPa, a yield stress at 33.3 ± 1.48 MPa, and a strain‐at‐failure 10.3 ± 0.61%, which are 45%, 40%, 32%, and 68% higher than neat PMA, respectively. This provides a significant improvement in toughness at 4.92 ± 0.55 MJ m −3 for the composite, 184% higher than that of neat PMA. The marked increase in toughness is due to enhanced filler‐matrix interactions which improve the ability of the 3D printed composite to absorb energy under tensile load. The results from this work provide new understandings into the strategies for design and preparation of stereolithography 3D printed materials reinforced with toughening fillers from renewable resources.