Premium
Direct Synthesis of Controlled Poly(styrene‐ co ‐acrylic acid)s of Various Compositions by Nitroxide‐Mediated Random Copolymerization
Author(s) -
Couvreur Laurence,
Charleux Bernadette,
Guerret Olivier,
Magnet Stéphanie
Publication year - 2003
Publication title -
macromolecular chemistry and physics
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.57
H-Index - 112
eISSN - 1521-3935
pISSN - 1022-1352
DOI - 10.1002/macp.200350065
Subject(s) - comonomer , copolymer , styrene , acrylic acid , polymer chemistry , chemistry , reactivity (psychology) , monomer , molar mass , dispersity , nitroxide mediated radical polymerization , radical polymerization , organic chemistry , polymer , medicine , alternative medicine , pathology
Styrene and acrylic acid were copolymerized under controlled conditions, in 1,4‐dioxane solution at 120 °C and 2 bar, using an alkoxyamine initiator based on the N ‐ tert ‐butyl‐ N ‐(1‐diethylphosphono‐2,2‐dimethylpropyl) nitroxide, SG1. A broad composition range from 90/10 to 10/90 was investigated. With slightly different initiator concentrations and a similar initial proportion of free SG1 (4.5 mol‐% with respect to the initiator) the polymerizations exhibited very similar rates, irrespective of the proportion of acrylic acid in the comonomer mixture (80% conversion within 8 h). In all cases, the copolymers presented number average molar masses, $\overline M _{\rm n}$ , that increased linearly with overall monomer conversion, and polydispersity indexes that ranged between 1.2 and 1.4. Moreover, $\overline M _{\rm n}$ followed the calculated values, based on the initial concentrations of monomers and initiator. The variation in the initiator concentration allowed to target various molar masses, but some limitation appeared at low initiator concentration owing to chain transfer to 1,4‐dioxane. From the kinetic data, the reactivity ratios were determined: r A = 0.27 ± 0.07 for acrylic acid and r S = 0.72 ± 0.04 for styrene. Depending on the initial comonomer composition, chains exhibited no or small composition drift, and hence a slightly pronounced gradient structure.Reactivity ratios for acrylic acid and styrene.