Mapping the initial corrosion activity of aluminium alloy 2024‐T3 in diluted substitute ocean water by localized electrochemical impedance spectroscopy
Author(s) -
Acosta Gloria,
Veleva Lucien,
de la Fuente Daniel
Publication year - 2018
Publication title -
materials and corrosion
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.487
H-Index - 55
eISSN - 1521-4176
pISSN - 0947-5117
DOI - 10.1002/maco.201810109
Subject(s) - corrosion , dielectric spectroscopy , alloy , materials science , chloride , aluminium , electrochemistry , metallurgy , nucleation , aluminium alloy , chemical engineering , chemistry , electrode , organic chemistry , engineering
This work deals with the initial localized corrosion activity of AA2024‐T3 exposed up to 24 h in diluted substitute ocean water, simulating marine environment of low chloride contamination. The pits appeared since the first hour at the periphery of CuFeMn particles and Mg‐ions release was found to be 0.5 mg L −1 , originated from the S‐phase (Al 2 CuMg). Fine particles were detached from the corrosion layer, composed of AlCl 3 · 6H 2 O and FeCl 2 · 2H 2 O corrosion products. Localized electrochemical impedance spectroscopy (LEIS) measurements were performed in situ at open circuit potential. LEIS maps revealed intensive electrochemical activity on Al alloy surface since the first hour, demonstrating fast pit nucleation, due to the presence of chloride ions. LEIS impedance │Z│ magnitude differs with the advance of the corrosion process, influenced by changes occurring on the alloy surface. The reported results confirm the unique capabilities of LEIS that make this a powerful tool for in situ study of localized corrosion process.