High temperature corrosion investigation in an oxyfuel combustion test rig
Author(s) -
Montgomery M.,
Bjurman M.,
Hjørnhede A.,
Rombrecht H. B.,
Lisk A.,
Krautz H. J.
Publication year - 2015
Publication title -
materials and corrosion
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.487
H-Index - 55
eISSN - 1521-4176
pISSN - 0947-5117
DOI - 10.1002/maco.201307245
Subject(s) - metallurgy , corrosion , materials science , high temperature corrosion , austenite , boiler (water heating) , alloy , combustion , oxide , austenitic stainless steel , microstructure , chemistry , waste management , organic chemistry , engineering
Oxyfuel firing and subsequent capture of CO 2 is a way to reduce CO 2 emissions from coal‐fired boilers. Literature is summarized highlighting results which may contribute to understanding of the corrosion processes in an oxyfuel boiler. Tests were conducted in a 500 kWth oxyfuel test facility constructed by Brandenburg Technical University to gain understanding into oxyfuel firing. Two air‐cooled corrosion probes were exposed in this oxyfuel combustion chamber where the fuel was lignite. Gas composition was measured at the location of testing. Various alloys from a 2 1 2Cr steel, austenitic steels to nickel alloys were exposed at set metal temperatures of 570 and 630 °C for 287 h. The specimens were investigated using light optical and scanning electron microscopy and X‐ray diffraction. The deposit on the probe contained predominantly CaSO 4 and Fe 2 O 3 . Oxide thickness and depth of the precipitated (perhaps carburized) zone was used as a measure of corrosion rates. The lowest alloyed steel had the highest corrosion rate, and the other austenitic and nickel alloys had much lower corrosion rates. Precipitates in the alloy adjacent the corrosion front were revealed for both Sanicro 28 and C‐276. However, it was observed that precipitates were present on both the concave and fireside convex tube surfaces, thus oxyfuel conditions cannot be responsible for these precipitations.