The role that bond coat depletion of aluminum has on the lifetime of APS‐TBC under oxidizing conditions
Author(s) -
Renusch D.,
Schorr M.,
Schütze M.
Publication year - 2008
Publication title -
materials and corrosion
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.487
H-Index - 55
eISSN - 1521-4176
pISSN - 0947-5117
DOI - 10.1002/maco.200804137
Subject(s) - spallation , materials science , thermal barrier coating , oxidizing agent , composite material , coating , aluminium , forensic engineering , chemistry , physics , organic chemistry , quantum mechanics , neutron , engineering
Bond coat oxidation as well as bond coat depletion of Al are still believed to be a major degradation mechanism with respect to the lifetime of thermal barrier coating (TBC) systems. In this study the top coat lifetime is described as being limited by both bond coat depletion of Al and mechanical failure of the top coat. The empirical results are introduced by considering three spallation cases, namely, Al depletion failure, thermal fatigue failure, and thermal aging failure. Al depletion failure occurs when the Al content within the bond coat reaches a critical value. In this paper bond coat depletion of Al is modeled by considering the diffusion of Al into both the thermally grown oxide (TGO) and substrate. The diffusion model results are compared to Al concentration profiles measured with an electron beam microprobe. These measured results are from oxidized air plasma sprayed TBC systems (APS‐TBC) with vacuum plasma sprayed (VPS) bond coats for exposures up to 5000 h in the temperature range of 950–1100 °C. This paper focuses on the Al depletion failure and how it relates to top coat spallation.