Influence of chromium, molybdenum and cobalt on the corrosion behaviour of high carbon steels in dependence of heat treatment
Author(s) -
Peissl S.,
Mori G.,
Leitner H.,
Ebner R.,
Eglsäer S.
Publication year - 2006
Publication title -
materials and corrosion
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.487
H-Index - 55
eISSN - 1521-4176
pISSN - 0947-5117
DOI - 10.1002/maco.200503969
Subject(s) - tempering , materials science , metallurgy , chromium , corrosion , carbide , molybdenum , martensite , cobalt , precipitation hardening , microstructure , martensitic stainless steel , chromium carbide , precipitation , physics , meteorology
High chromium martensitic steels are designed to provide high corrosion resistance in combination with high strength. Some of these steel grades contain primary carbides for improving the wear resistance, e.g. the steel 440C. The present paper mainly deals with the effect of chemical composition and microstructure on the corrosion properties. Different experimental alloys were produced in the shape of small ingots. The influence of the alloying elements chromium, molybdenum, cobalt, and carbon on the corrosion properties was studied. The results can be summarized as follows: Chromium and molybdenum improve the corrosion resistance, however, only the content of these elements in solid solution in the steel matrix is effective. In case of cobalt the corrosion resistance decreases. The reason is the interaction between cobalt and carbon and its effect on the chromium content in the steel matrix. The calculated pitting resistant equivalent number of high chromium martensitic steels is only limited valid, because there is a major effect of carbide precipitation on the corrosion behaviour. Further investigations were focused on the heat treatment. Especially the effect of the tempering temperature of these steels was studied. The tempering temperature is most relevant for secondary hardening carbide precipitation, which lowers the chromium content of the matrix with detrimental influence on the corrosion properties. The carbide precipitation and chromium distribution was characterized by means of energy filtered transmission electron microscopy (EFTEM).