Open AccessEffect of different firing atmospheres on debonding strength of dental porcelain fused to commercially pure titanium
Author(s) -
Wang JenChyan,
Fu PoSung,
Lai PeiLing,
Liu ChenShih,
Chen WenCheng,
Hung ChunCheng
Publication year - 2020
Publication title -
the kaohsiung journal of medical sciences
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.439
H-Index - 36
eISSN - 2410-8650
pISSN - 1607-551X
DOI - 10.1002/kjm2.12157
Subject(s) - bond strength , titanium , composite material , materials science , indentation hardness , argon , bonding strength , metallurgy , microstructure , adhesive , physics , layer (electronics) , atomic physics
An in vitro investigation was performed to evaluate the bonding characteristics of porcelain fused to metal (PFM)/commercially pure titanium (cp Ti, grade II) in three firing atmospheres of under vacuum and using two noble gases argon (Ar) and helium (He). Three groups of porcelain veneers firing under vacuum, Ar, and He were prepared to evaluate the bonding of porcelain fused to the cold‐rolled cp Ti. The bond strength of PFM durability by a three‐point bending test, phases, microhardness of cp Ti after firing processes, and fractures were measured and evaluated. Results show the microhardness of cp Ti in group of porcelain firing under He atmosphere was significantly lower than that of the two other groups, which were in vacuum and Ar ( P < .05). X‐ray diffraction showed the He group produced in relatively small amounts of TiO 2 and TiO oxides than other groups but featured relatively high quantity of airhole defects in the porcelain body leading to the lowest bond strength. The Ar group presented the highest bond strength of comparing with the groups under vacuum and using He ( P < .05). Although the firing processes in He could efficiently prevent the diffusion of oxygen into Ti, the porcelain‐cp Ti bond strength using Ar protective atmosphere presented the advantage to achieve clinical requirement because porcelain firing under He revealed prominent voids and defects within the body of porcelain.