New multicolor and rewritable holographic polymer film for three‐dimensional holographic display
Author(s) -
Miura Sakiko,
Kobayashi Satoshi
Publication year - 2014
Publication title -
journal of the society for information display
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.578
H-Index - 52
eISSN - 1938-3657
pISSN - 1071-0922
DOI - 10.1002/jsid.262
Subject(s) - holography , materials science , diffraction efficiency , polymer , optics , holographic data storage , photographic emulsion , silver halide , diffraction , optoelectronics , holographic display , composite material , physics , layer (electronics)
We have developed a new multicolor holographic polymer film. Our holographic polymer film contains 3‐[(2,4,6‐trichloro)azo]‐9H‐carbazole‐9‐ethanol (A‐1) and poly(methyl methacrylate). The holographic polymer film can be recorded with a holographic image without applying an external electric field. The diffraction efficiency was 57% at A‐1 with a 20 wt% of dope ratio. The writable holographic image writing for the holographic polymer film step used the silver halide photographic emulsion master plate 532‐nm laser beam under the nonelectric field. After the copy hologram is formed, our holographic polymer film can be displayed in red and green holographic images. Even though our holographic polymer film is rewritten over 200 times, the diffraction efficiency does not fall. As the holographic polymer film is manufactured using roll‐to‐roll techniques, although still in a laboratory scale in this study, it has a strong possibility of being manufactured in larger sizes with lower cost.