Raman investigations of TiO 2 nanotube substrates covered with thin Ag or Cu deposits
Author(s) -
Roguska A.,
Kudelski A.,
Pisarek M.,
Lewandowska M.,
Dolata M.,
JanikCzachor M.
Publication year - 2009
Publication title -
journal of raman spectroscopy
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.748
H-Index - 110
eISSN - 1097-4555
pISSN - 0377-0486
DOI - 10.1002/jrs.2314
Subject(s) - nanotube , raman spectroscopy , auger electron spectroscopy , scanning electron microscope , materials science , substrate (aquarium) , analytical chemistry (journal) , adsorption , layer (electronics) , chemical engineering , nanotechnology , chemistry , carbon nanotube , composite material , organic chemistry , oceanography , physics , engineering , geology , nuclear physics , optics
A tubular array of TiO 2 nanotubes on Ti matrix was used as a support for Ag or Cu sputter‐deposited layers intended for surface‐enhanced Raman scattering (SERS) investigations. The composite samples of Ag/TiO 2 –nanotube/Ti and Cu/TiO 2 –nanotube/Ti were studied with the aid of scanning electron microscopy (SEM) and Auger electron spectroscopy (AES) [and scanning Auger microscopy (SAM)] to reveal their characteristic morphological and chemical features. Raman spectra of pyridine (as a probe molecule) were measured after it had been adsorbed on the TiO 2 –nanotube/Ti substrates covered with thin Ag or Cu deposit as well as on the bulk electrochemically roughened Ag or Cu reference substrates. It was found that the SERS spectra measured for pyridine adsorbed on the bulk silver substrate were significantly different than the spectra measured on the TiO 2 –nanotube/Ti substrates covered the Ag layer. The spectra measured for pyridine adsorbed on the Ag/TiO 2 –nanotube/Ti suggest that on the surface of such a composite substrate there are many Lewis acidic sites. Spectra typical for pyridine adsorbed on acidic sites were observed even after deposition of a relatively thick silver layer (e.g. an Ag layer with an average thickness of 80 nm) on the TiO 2 –nanotube/Ti support. Our findings suggest that TiO 2 –nanotube/Ti support is a promising substrate for the preparation of metallic nano‐clusters on a support containing acidic active sites. Copyright © 2009 John Wiley & Sons, Ltd.