Resin–tooth interfacial morphology and sealing ability of one‐step self‐etch adhesives: Microleakage and SEM study
Author(s) -
Manuja Naveen,
Nagpal Rajni
Publication year - 2012
Publication title -
microscopy research and technique
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.536
H-Index - 118
eISSN - 1097-0029
pISSN - 1059-910X
DOI - 10.1002/jemt.22011
Subject(s) - enamel paint , materials science , adhesive , dentin , scanning electron microscope , phosphoric acid , dentistry , morphology (biology) , composite material , layer (electronics) , metallurgy , medicine , biology , genetics
OBJECTIVES: To compare microleakage of three self‐etch adhesives and to analyze enamel surface morphology and interfacial morphology of resin–enamel and resin–dentin interface under scanning electron microscope (SEM). EXPERIMENTAL DESIGN: Study was conducted in 65 extracted human premolars. Class V cavities were prepared in 45 teeth and assigned to three groups ( n = 15) according to three self‐etch adhesives (OptiBond All‐in‐One, iBond, and Adper Prompt L‐Pop). After restoration, 10 samples from each group were used to assess microleakage at enamel and dentin margin. Five samples from each group were used for analysis of interfacial morphology at resin–enamel and resin–dentin interface under SEM. Remaining 20 teeth were used to prepare flat enamel buccal surfaces to analyze the difference in surface morphology after treatment with three adhesives ( n = 5 each) and 36% phosphoric acid treatment ( n = 5). PRINCIPAL OBSERVATIONS: At enamel margin, Prompt L‐Pop depicted least leakage of all the three adhesives and also showed best interfacial adaptation under SEM. At dentin margin, OptiBond All‐in‐One showed significant less leakage than iBond and Prompt L‐Pop. On flat enamel surface, phosphoric acid produced the most retentive etching pattern when compared with the three adhesives. CONCLUSION: Prompt L‐Pop showed the best bonding effectiveness in enamel, whereas OptiBond All‐in‐One performed significantly better in dentin. Microsc. Res. Tech. 2012. © 2012 Wiley Periodicals, Inc.