Degradation of zinc in saline solutions, plasma, and whole blood
Author(s) -
Törne Karin,
Larsson Mariann,
Norlin Anna,
Weissenrieder Jonas
Publication year - 2016
Publication title -
journal of biomedical materials research part b: applied biomaterials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.665
H-Index - 108
eISSN - 1552-4981
pISSN - 1552-4973
DOI - 10.1002/jbm.b.33458
Subject(s) - corrosion , zinc , electrolyte , zinc phosphate , whole blood , passivation , materials science , saline , plasma , simulated body fluid , degradation (telecommunications) , layer (electronics) , chemistry , metallurgy , composite material , electrode , surgery , scanning electron microscope , endocrinology , medicine , physics , quantum mechanics , telecommunications , computer science
The initial degradation of zinc has been investigated through exposures to simulated and real body fluids of increasing complexity: phosphate buffered saline (PBS), Ringer's saline solution, human plasma, and whole blood. Real body fluids were used to close the electrolyte gap between simulated and in vivo environment. Polarization of zinc in whole blood show a passive response not present in other electrolytes. The analysis shows a decrease in corrosion rate with time for plasma and whole blood and an increase for PBS and Ringer's. During exposure to plasma and whole blood a bi‐layered corrosion product with poor adherence was formed over a uniformly corroding surface. The corrosion products comprise a mixture of inorganic material and biomolecules. Samples degrading in PBS were prone to localized corrosion and formed thick porous corrosion products of primarily zinc phosphates while in Ringer's solution a gel like layer of zinc carbonate was formed over an interface with shallow pits. The use of whole blood or plasma as electrolytes for short term in vitro evaluation of potential biodegradable metals may provide an improved understanding of the behavior in vivo , while Ringer's solution is preferred over PBS for long term degradation studies of zinc. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1141–1151, 2016.