In vitro biodegradation behavior, mechanical properties, and cytotoxicity of biodegradable Zn–Mg alloy
Author(s) -
Gong Haibo,
Wang Kun,
Strich Randy,
Zhou Jack G.
Publication year - 2015
Publication title -
journal of biomedical materials research part b: applied biomaterials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.665
H-Index - 108
eISSN - 1552-4981
pISSN - 1552-4973
DOI - 10.1002/jbm.b.33341
Subject(s) - extrusion , biodegradation , materials science , biocompatibility , alloy , microstructure , metallurgy , corrosion , magnesium alloy , zinc , magnesium , chemistry , organic chemistry
Zinc–Magnesium (Zn–Mg) alloy as a novel biodegradable metal holds great potential in biodegradable implant applications as it is more corrosion resistant than Magnesium (Mg). However, the mechanical properties, biodegradation uniformity, and cytotoxicity of Zn–Mg alloy remained as concerns. In this study, hot extrusion process was applied to Zn–1 wt % Mg (Zn–1Mg) to refine its microstructure. Effects of hot extrusion on biodegradation behavior and mechanical properties of Zn–1Mg were investigated in comparison with Mg rare earth element alloy WE43. Metallurgical analysis revealed significant grain size reduction, and immersion test found that corrosion rates of WE43 and Zn–1Mg were reduced by 35% and 57%, respectively after extrusion. Moreover, hot extrusion resulted in a much more uniform biodegradation in extruded Zn–1Mg alloy and WE43. In vitro cytotoxicity test results indicated that Zn–1Mg alloy was biocompatible. Therefore, hot extruded Zn–1Mg with homogenous microstructure, uniform as well as slow degradation, improved mechanical properties, and good biocompatibility was believed to be an excellent candidate material for load‐bearing biodegradable implant application. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 103B: 1632–1640, 2015.