Colorless and high strength MgO/Al 2 O 3 /SiO 2 glass–ceramic dental material using zirconia as nucleating agent
Author(s) -
Dittmer Marc,
Rüssel Christian
Publication year - 2012
Publication title -
journal of biomedical materials research part b: applied biomaterials
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.665
H-Index - 108
eISSN - 1552-4981
pISSN - 1552-4973
DOI - 10.1002/jbm.b.31972
Subject(s) - cubic zirconia , ceramic , materials science , composite material , glass ceramic , flexural strength , nucleation , mineralogy , chemical engineering , chemistry , organic chemistry , engineering
Abstract Glasses in the system of MgO/Al 2 O 3 /SiO 2 with different concentrations of zirconia as nucleating agent, some of them additionally doped with ZnO or P 2 O 5 , were annealed in a temperature range from 950 to 1150°C. The use of zirconia led to colorless glass–ceramics, which were transparent to opaque. In all studied compositions, α‐/β‐quartz‐solid‐solutions, zirconia as well as spinel or gahnite (ZnAl 2 O 4 )/spinel‐solid‐solution precipitated. The highest bending strength of 475 MPa was obtained after annealing at 1000°C for 3 h. The increase of the annealing temperature or an increase in the zirconia concentration resulted in an increase of the microhardness up to 13.3 GPa and of the fracture toughness up to 2.7 MPa m 1/2 . The addition of ZnO results in an increase of the hardness up to 12.5 GPa. The addition of ZnO or P 2 O 5 led to a fracture toughness of 2 MPa m 1/2 . The described physical properties had to be highly advantageous for the preparation of colorless high strength dental glass–ceramics. © 2011 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 100B: 463–470, 2012.